The aim of this work is to study and model the effect of three aging factors, temperature, humidity and light radiation, on the properties of a fabric made of a blend of Kevlar® and PBI fibers frequently used to manufacture fire-protective garments. Accelarated-aging treatments carried out at carefully chosen conditions for the three factors resulted in a sizeable loss of mechanical performance. The breaking force of both the fabric and the yarns extracted from it decreases to less than 50% after one month of continuous exposure. X-ray diffraction (XRD) tests performed on thermally-aged samples indicated an increase of the crystallinity of the fabric, whereas the disappearance of Raman spectral lines suggested instead a reduction of the crystallinity following thermal aging. To explain these seemingly contradictory results, a hypothesis was introduced, stating that two different processes occurred simultaneously during thermal aging. The first one, an increase of size of the crystallites in the direction of the fibers’ axis, accounted for the increase in crystallinity observed in XRD tests. The second one, an increase in the gap separating lamellar crystallites that causes a non-measurable reduction of the crystallinity of the sample, was highlighted by the Raman analyses. The results of the dielectric spectroscopy analyses carried out on thermally-aged samples confirmed the XRD results showing a significant change in the Kevlar’s morphology during thermal aging. Despite the important decrease of the breaking force that ensued thermal aging, no evidence of a chemical structure modification of Kevlar® was found. On the other hand, differential thermal analyses conducted on thermally aged fabric samples indicated a reduction of the glass transition temperature of the other component of the blend, namely the PBI, a fact that suggests a decrease of molecular weight after thermal aging. Infrared spectroscopy analyses performed on samples exposed to high humidity levels showed the development of a new absorbing band in the spectrum of aged Kevlar® yarns. This band was ascribed to the formation of carboxylic acid groups. Based on these results, the humidity aging mechanism was inferred. This mechanism corresponds to the hydrolysis of the amide bond of Kevlar® catalyzed by an acid. The progress of the hydrolysis reaction was modeled mathematically using the evolution of the concentration of carboxylic acid groups. The mechanism of light radiation aging was also determined from infrared spectroscopy analyses as the absorbing band attributed to the carboxylic acid groups was once again observed. In the case of light radiation, the degradation mechanism corresponds to a photo-oxidation reaction initiated by the photolysis of the amide bond of Kevlar®. The accumulation of Photo-Fries products on the surface of yarns is believed to slow down of the oxidation reaction, as indicated by the overlapping of breaking force vs. aging time curves for the light-radiation aged samples. Expressions based on the Arrhenius law were used to characterize both the thermal and hydrolytic aging, whereas an expression taking into account the irradiance as well as the temperature was used to model the light radiation aging. The global damage produced by the joint action of the three aging factors was modeled after Palmgren-Miner’s linear cumulative damage theory.
| Date | 5 May 2011 |
|---|
| Original language | French |
|---|
| Awarding Institution | - École de technologie supérieure
|
|---|
| Supervisor | Éric David (Supervisor) & Toan Vu-Khanh (Co-supervisor) |
|---|
Arrieta, C. (Author),
David (Supervisor) & Vu-Khanh (Co-supervisor),
5 May 2011Student thesis: Doctoral thesis › Doctorate in Engineering: Engineering