Amélioration de l'adhésion de revêtements organiques déposés par plasma froid sur polymères pour applications biomédicales

Abstract

Plasma surface modification is commonly used in biomedical field, for example to enhance cell adhesion and growth surrounding the stent covers without affecting its bulk properties. Plasma polymer (PP) deposition used to create thin films rich in functional groups, e.g. primary amines, known to enhance the cellular response and allow grafting of biomolecules especially on stent grafts. Thin film adhesion to stent polymeric cover should be considered especially as they will evolve in a biological environment. The aim of this project is to evaluate the adhesion of PP on polytetrafluoroethylene (PTFE) and polyethyleneterephthalate (PET). Thereafter, an ammonia plasma treatment on PTFE is performed prior to deposition of PP to optimize the PP/PTFE adhesion. PP studied here (referred to as "LP") is prepared from a mixture of ethylene (C2H4) and ammonia (NH3). It is deposited on two supports, PET and PTFE. The interfacial adhesion between the LP coating and the substrate was evaluated by "Peel-test 180 °" according to ASTM F1842. Staining of the surface after peel test followed by an image analysis was performed to determine the percentage of removed coating. Adhesion optimization is done by varying operating plasma parameters such as power, pressure and pretreatment time. Chemical analyses and wettability of LP and pretreated surfaces in dry and wet conditions are characterized by XPS and contact angle measurements, respectively. The adhesion of LP/PET was excellent in a dry environment (<1%), but lower under wet conditions (4±6% and 44±7% as minimum and maximum values at 5min and 60min of immersion in deionized water, respectively). However, 56% to 75% of the LP is removed from virgin PTFE in a dry and wet environment, respectively; percentages can be substantially reduced by plasma pretreatment (0% and 8±3% in air and 30min in deionized water). Almost no delamination was observed with NH3 plasma pretreatment at 15s, 100 mTorr and 50W. N2 plasma pretreatment, for comparison, proves much less effective. The LP/PTFE adhesion is considerably improved by plasma pretreatment compared to untreated samples. The chemical LP composition and the cell growth on LP/pretreated PTFE are not significantly affected by this pretreatment. Further investigations are required to explain the LP/PET low adhesion in wet conditions.

Date	3 May 2013
Original language	French
Awarding Institution	École de technologie supérieure
Supervisor	Sophie Lerouge (Supervisor)