Effet de l'usinage sur les propriétés mécaniques en tension et contrôle non-destructif des matériaux composites

Abstract

The main goal of this work is to evaluate the impact of milling operations on the integrity of unidirectional carbon/epoxy laminate. Milling, often used for finishing composite structures, cause some damage in the form of craters, cracks and thermal damage to the matrix. Here, two approaches are used to qualify and quantify the amount of damage. First, two nondestructive testing methods, namely immersion ultrasonic inspection and pulsed thermography, are evaluated on samples with artificial defects. These techniques are then used on machined samples with realistic machining damages. Only ultrasounds allowed the detection and quantification of the machining damages, but only if the damages are at the surface of the laminate. The depth of damage depends primarily on the fiber orientation of the first ply with respect to the cutting direction. The ultrasonic inspections are also accompanied by scanning electron microscope observations. The second approach is to check whether the presence of the machining damage will affect the mechanical properties of the laminate. To do this, static tensile tests are performed on samples prepared by three different methods, namely, by abrasive diamond saw, by saw cut followed by sanding and finally by milling. The results show that the damages caused by the milling operation are not important enough to affect the ultimate stress and elastic modulus. Despite this, it would be interesting, for future works, to investigate this aspect in fatigue rather than with static tests. The presence of damages on the edge might promote delamination during cyclic loads.

Date	4 Dec 2012
Original language	French
Awarding Institution	École de technologie supérieure
Supervisor	Martin Viens (Supervisor) & Gilbert Lebrun (Co-supervisor)