Effect of Fe Concentration and Superheating on the Microstructure and Tensile Properties of High Mg 413.0-Type Alloys: Role of Sr, Be, P, and La

Keyphrases

• Aluminum Matrix 33%
• As-cast Condition 33%
• Base Alloy 33%
• Cast Al-Si Alloy 33%
• Fe Concentration 100%
• Ferrosilicon 33%
• Hard Phase 33%
• Harmful Effects 33%
• High Iron Content 33%
• High Strength 33%
• Iron Content 33%
• Melt Treatment 33%
• Metallographic Examination 33%
• Microstructure Properties 100%
• Optimum Quality 33%
• Platelets 33%
• Primary Si 33%
• Quality Value 33%
• Set-aside 33%
• Solidification Rate 100%
• Sr Addition 33%
• Strength Quality 33%
• T6 Treatment 33%
• Tensile Properties 100%
• Tensile Strength 33%
• Tensile Test 33%

Engineering

• Aluminum Matrix 33%
• Base Alloy 33%
• Cast Condition 33%
• Hard Phase 33%
• Harmful Effect 33%
• Iron 33%
• Iron Content 66%
• Metallographic Examination 33%
• Phase Particle 33%
• Platelet 33%
• Process Step 33%
• Solidification Rate 100%
• Tensile Bar 33%
• Tensile Property 100%
• Tensile Testing 33%
• Ultimate Tensile Strength 33%

Material Science

• Aluminum 33%
• Platelet 33%
• Silicon Alloys 33%
• Solidification 100%
• Tensile Property 100%
• Tensile Testing 33%
• Ultimate Tensile Strength 33%